Abstract: | The creation of three-dimensionally engineered nanoporous architectures via covalently interconnected nanoscale building blocks remains one of the fundamental challenges in nanotechnology. Here we report the synthesis of ordered, stacked macroscopic three-dimensional (3D) solid scaffolds of graphene oxide (GO) fabricated via chemical cross-linking of two-dimensional GO building blocks. The resulting 3D GO network solids form highly porous interconnected structures, and the controlled reduction of these structures leads to formation of 3D conductive graphene scaffolds. These 3D architectures show promise for potential applications such as gas storage; CO2 gas adsorption measurements carried out under ambient conditions show high sorption capacity, demonstrating the possibility of creating new functional carbon solids starting with two-dimensional carbon layers |
Description: | ACS nano,VOL 7,issue 8,pp 7034-7040 |
URI: | http://dyuthi.cusat.ac.in/purl/4385 |
Files | Size |
---|---|
Covalently Inte ... Graphene Oxide Solids.pdf | (1.180Mb) |
Abstract: | In this letter, we report flexible, non corrosive, and light weight nickel nanoparticle@multi-walled carbon nanotube–polystyrene (Ni@MWCNT/PS) composite films as microwave absorbing material in the frequency range of S band (2-4 GHz). Dielectric permittivity and magnetic permeability of composites having 0.5 and 1.5 wt. % filler amount were measured using the cavity perturbation technique. Reflection loss maxima of 33 dB (at 2.7 GHz) and 24 dB (at 2.7 GHz) were achieved for 0.5 and 1.5 wt. % Ni@MWCNT/PS composite films of 6 and 4 mm thickness, respectively, suggesting that low concentrations of filler provide significant electromagnetic interference shielding |
Description: | APPLIED PHYSICS LETTERS 99, 113116 (2011) |
URI: | http://dyuthi.cusat.ac.in/purl/4363 |
Files | Size |
---|---|
Ni filled flexi ... nt microwave absorbers.pdf | (2.017Mb) |