| Abstract: | Thermal diffusivity (TD) measurements were performed on some industrially important dyes – auramine O (AO), malachite green and methylene blue (MB) – adsorbed K-10 montmorillonites using photoacoustic method. The TD value for the dye-adsorbed clay mineral was observed to change with a variation in dye concentration. The contribution of the dye towards TD was also determined. The repeatedly adsorbed samples with MB and AO exhibited a lower TD than the single-adsorbed samples. TD values of sintered MB samples were also obtained experimentally. These sintered samples exhibit a higher TD, although they show a trend similar to that of non-sintered pellets. A variation in dye concentration and sintering temperature can be used for tuning the TD value of the clay mineral to the desired level. |
| URI: | http://dyuthi.cusat.ac.in/purl/2621 |
| Files | Size |
|---|---|
| Dyuthi-P0182.pdf | (398.5Kb) |
| Abstract: | Thermal diffusivity (TD) measurements were performed on some industrially important dyes – auramine O (AO), malachite green and methylene blue (MB) – adsorbed K-10 montmorillonites using photoacoustic method. The TD value for the dye-adsorbed clay mineral was observed to change with a variation in dye concentration. The contribution of the dye towards TD was also determined. The repeatedly adsorbed samples with MB and AO exhibited a lower TD than the single-adsorbed samples. TD values of sintered MB samples were also obtained experimentally. These sintered samples exhibit a higher TD, although they show a trend similar to that of non-sintered pellets. A variation in dye concentration and sintering temperature can be used for tuning the TD value of the clay mineral to the desired level |
| Description: | Philosophical Magazine Vol. 89, No. 10, 1 April 2009, 895–905 |
| URI: | http://dyuthi.cusat.ac.in/purl/3998 |
| Files | Size |
|---|---|
| Thermal charact ... d K-10 montmorillonite.pdf | (388.6Kb) |
| Abstract: | Thermal characterization of alumina–zirconia and zirconia ceramic tapes using a photoacoustic technique is presented. A transmission-mode geometry is employed for the measurement of thermal diffusivity while a reflection-mode geometry is used for the measurement of thermal effusivity. In both these geometries, the same open photoacoustic cell is used. From the measured values of thermal diffusivity and thermal effusivity, the thermal conductivity value has also been evaluated. |
| URI: | http://dyuthi.cusat.ac.in/purl/2612 |
| Files | Size |
|---|---|
| Dyuthi-P0172.pdf | (353.2Kb) |
| Abstract: | Thermal diffusivity of the composites of camphor sulphonic acid (CSA) doped polyaniline (PANI) and its composites with cobalt phthalocyanine (CoPc) has been measured using open cell photoacoustic technique. Analysis of the data shows that the effective thermal diffusivity value can be tuned by varying the relative volume fraction of the constituents. It is seen that polaron assisted heat transfer mechanism is dominant in CSA doped PANI and these composites exhibit a thermal diffusivity value which is intermediate to that of CSA doped PANI and CoPc. The results obtained are correlated with the electrical conductivity and hardness measurements carried out on the samples. |
| URI: | http://dyuthi.cusat.ac.in/purl/1828 |
| Files | Size |
|---|---|
| Thermal charact ... s composites with CoPc.pdf | (45.66Kb) |
| Abstract: | Thermal diffusivity of the composites of camphor sulphonic acid (CSA) doped polyaniline (PANI) and its composites with cobalt phthalocyanine (CoPc) has been measured using open cell photoacoustic technique. Analysis of the data shows that the effective thermal diffusivity value can be tuned by varying the relative volume fraction of the constituents. It is seen that polaron assisted heat transfer mechanism is dominant in CSA doped PANI and these composites exhibit a thermal diffusivity value which is intermediate to that of CSA doped PANI and CoPc. The results obtained are correlated with the electrical conductivity and hardness measurements carried out on the samples |
| URI: | http://dyuthi.cusat.ac.in/purl/1827 |
| Files | Size |
|---|---|
| Dyuthi-P00385.pdf | (45.66Kb) |
| Abstract: | An open photoacoustic cell operating in the low range of chopping frequency has been employed to evaluate the thermal diffusivity values of intrinsic InP and InP doped with S, Sn and Fe. The experimental set-up is calibrated by the evaluation of thermal diffusivity value of pure Si and GaAs. The present investigation shows that doped samples show a reduced value for thermal diffusivity compared to intrinsic sample. From the analysis of data it is also seen that nature of dopant clearly influences the thermal diffusivity value of semiconductors. The results are explained in terms of phonon assisted heat transfer mechanism in semiconductors |
| URI: | http://dyuthi.cusat.ac.in/purl/1832 |
| Files | Size |
|---|---|
| Dyuthi-P0249.pdf | (64.36Kb) |
| Abstract: | An open photoacoustic cell operating in the low range of chopping frequency has been employed to evaluate the thermal diffusivity values of intrinsic InP and InP doped with S, Sn and Fe. The experimental set-up is calibrated by the evaluation of thermal diffusivity value of pure Si and GaAs. The present investigation shows that doped samples show a reduced value for thermal diffusivity compared to intrinsic sample. From the analysis of data it is also seen that nature of dopant clearly influences the thermal diffusivity value of semiconductors. The results are explained in terms of phonon assisted heat transfer mechanism in semiconductors |
| URI: | http://dyuthi.cusat.ac.in/purl/1831 |
| Files | Size |
|---|---|
| Thermal charact ... hotoacoustic technique.pdf | (64.36Kb) |
| Abstract: | An open photoacoustic cell operating in the low range of chopping frequency has been employed to evaluate the thermal diffusivity values of intrinsic InP and InP doped with S, Sn and Fe. The experimental set-up is calibrated by the evaluation of thermal diffusivity value of pure Si and GaAs. The present investigation shows that doped samples show a reduced value for thermal diffusivity compared to intrinsic sample. From the analysis of data it is also seen that nature of dopant clearly influences the thermal diffusivity value of semiconductors. The results are explained in terms of phonon assisted heat transfer mechanism in semiconductors |
| URI: | http://dyuthi.cusat.ac.in/purl/1833 |
| Files | Size |
|---|---|
| Thermal charact ... hotoacoustic technique.pdf | (64.36Kb) |
| Abstract: | Thermal diffusivity (TD) measurement on commercial K-10 and KSF montmorillonites was carried out by photoacoustic technique. The TD of the montmorillonites after methylene blue adsorption changed with the dye concentration. The repeatedly adsorbed samples showed a lesser TD than the single adsorbed samples. After methylene blue adsorption the acid leached K-10 samples showed well defined changes in TD when compared to the ordered KSF samples |
| Description: | Applied Clay Science 42 (2009) 483–487 http://dx.doi.org/10.1016/j.clay.2008.06.006 |
| URI: | http://dyuthi.cusat.ac.in/purl/3999 |
| Files | Size |
|---|---|
| Thermal charact ... ed montmorillonites by.pdf | (325.8Kb) |
| Abstract: | Thermal diffusivity (TD) measurement on commercial K-10 and KSF montmorillonites was carried out by photoacoustic technique. The TD of the montmorillonites after methylene blue adsorption changed with the dye concentration. The repeatedly adsorbed samples showed a lesser TD than the single adsorbed samples. After methylene blue adsorption the acid leached K-10 samples showed well defined changes in TD when compared to the ordered KSF samples. |
| URI: | http://dyuthi.cusat.ac.in/purl/1756 |
| Files | Size |
|---|---|
| pdf 3.pdf | (325.8Kb) |
| Abstract: | A laser-induced photoacoustic technique was employed to investigate thermal transport through nanocrystalline CePO4 samples prepared via the sol–gel route. Evaluation of thermal diffusivity was carried out using the one-dimensional model of Rosencwaig and Gersho for the reflection configuration of the photoacoustic method. Structural analyses of samples revealed that they are nanoporous in nature, possessing micron-sized grains. Analysis of results shows that thermal diffusivity value varies with sintering temperature. Results are explained in terms of the variation in porosity with sintering temperature and the effects of various scattering mechanisms on the propagation of phonons through the nanoporous ceramic matrix. Further analyses confirm that apart from porosity, grain boundary resistance and interface thermal resistance influence the effective value of thermal diffusivity of the samples under investigation. |
| URI: | http://dyuthi.cusat.ac.in/purl/2423 |
| Files | Size |
|---|---|
| Dyuthi-P0275.pdf | (543.3Kb) |
| Abstract: | Dual beam mode-matched thermal lens method has been employed to measure the heat diffusion in nanofluid of silver with various volumes of rhodamine 6G, both dispersed in water. The important observation is an indication of temperature dependent diffusivity and that the overall heat diffusion is slower in the chemically prepared Ag sol compared to that of water. The experimental results can be explained assuming that Brownian motion is the main mechanism of heat transfer under the present experimental conditions. Light induced aggregation of the nanoparticles can also result in an anomalous diffusion behavior. |
| URI: | http://dyuthi.cusat.ac.in/purl/1755 |
| Files | Size |
|---|---|
| pdf 2.pdf | (352.2Kb) |
| Abstract: | The fluorescence spectrum of the schiff base obtained from salicylaldehyde and 2-aminophenol is studied using an argon-ion laser as the excitation source and its fluorescence quantum yield (Qf) is determined using a thermal lens method. This is a nondestructive technique that gives the absolute value of Qf without the need for a fluorescence standard. The quantum-yield values are calculated for various concentrations of the solution in chloroform and also for various excitation wavelengths. The value of Qf is relatively high, and is concentration dependent. The maximum value of Qf obtained is nearly 0.78. The high value of the fluorescence quantum yield will render the schiff base useful as a fluorescent marker for biological applications. Photostability and gain studies will assess its suitability as a laser dye. |
| URI: | http://dyuthi.cusat.ac.in/purl/2610 |
| Files | Size |
|---|---|
| Dyuthi-P0170.pdf | (449.8Kb) |
| Abstract: | In order to characterise the laser ablation process from high-Tc superconductors, the time evolution of plasma produced by a Q-switching Nd:YAG laser from a GdBa2Cu3O7 superconducting sample has been studied using spectroscopic and ion-probe techniques. It has been observed that there is a fairly large delay for the onset of the emission from oxide species in comparison with those from atoms and ions of the constituent elements present in the plasma. Faster decay occurs for emission from oxides and ions compared with that from neutral atoms. These observations support the view that oxides are not directly produced from the target, but are formed by the recombination process while the plasma cools down. Plasma parameters such as temperature and velocity are also evaluated. |
| URI: | http://dyuthi.cusat.ac.in/purl/2425 |
| Files | Size |
|---|---|
| Dyuthi-P0285.pdf | (500.6Kb) |
| Abstract: | In this paper, we describe the use of an open cell photoacoustic configuration for the evaluation of the thermal effusivity of liquid crystals. The feasibility, precision and reliability of the method are initially established by measuring the thermal effusivities of water and glycerol, for which the effusivity values are known accurately. In order to demonstrate the use of the present method in the thermal characterization of liquid crystals, we have measured the thermal effusivity values in various mesophases of 4-cyano-4 - octyloxybiphenyl (8OCB) and 4-cyano-4 -heptyloxybiphenyl (7OCB) liquid crystals using a variable temperature open photoacoustic cell. A comparison of the measured values for the two liquid crystals shows that the thermal effusivities of 7OCB in the nematic and isotropic phases are slightly less than those of 8OCB in the corresponding phases |
| URI: | http://dyuthi.cusat.ac.in/purl/1835 |
| Files | Size |
|---|---|
| Use of an open ... al characterisation of.pdf | (142.4Kb) |
| Abstract: | In this paper, we describe the use of an open cell photoacoustic configuration for the evaluation of the thermal effusivity of liquid crystals. The feasibility, precision and reliability of the method are initially established by measuring the thermal effusivities of water and glycerol, for which the effusivity values are known accurately. In order to demonstrate the use of the present method in the thermal characterization of liquid crystals, we have measured the thermal effusivity values in various mesophases of 4-cyano-4 - octyloxybiphenyl (8OCB) and 4-cyano-4 -heptyloxybiphenyl (7OCB) liquid crystals using a variable temperature open photoacoustic cell. A comparison of the measured values for the two liquid crystals shows that the thermal effusivities of 7OCB in the nematic and isotropic phases are slightly less than those of 8OCB in the corresponding phases |
| URI: | http://dyuthi.cusat.ac.in/purl/1836 |
| Files | Size |
|---|---|
| Use of an open ... al characterisation of.pdf | (142.4Kb) |
| Abstract: | In this paper, we describe the use of an open cell photoacoustic configuration for the evaluation of the thermal effusivity of liquid crystals. The feasibility, precision and reliability of the method are initially established by measuring the thermal effusivities of water and glycerol, for which the effusivity values are known accurately. In order to demonstrate the use of the present method in the thermal characterization of liquid crystals, we have measured the thermal effusivity values in various mesophases of 4-cyano-4 - octyloxybiphenyl (8OCB) and 4-cyano-4 -heptyloxybiphenyl (7OCB) liquid crystals using a variable temperature open photoacoustic cell. A comparison of the measured values for the two liquid crystals shows that the thermal effusivities of 7OCB in the nematic and isotropic phases are slightly less than those of 8OCB in the corresponding phases |
| URI: | http://dyuthi.cusat.ac.in/purl/1834 |
| Files | Size |
|---|---|
| Dyuthi-P0227.pdf | (142.4Kb) |
| Abstract: | he phenomenon of single beam mirage effect, otherwise known as photothermal deflection (PTD) effect using a He–Ne laser beam has been employed to detect phase transitions in some liquid crystals. It has been observed that anomalous changes in amplitude occur in the PTD signal level near the transition temperature. The experimental details and the results of measurements made in liquid crystals E8, M21 and M24 are given in this paper. |
| URI: | http://dyuthi.cusat.ac.in/purl/2394 |
| Files | Size |
|---|---|
| Dyuthi-P0203.pdf | (115.9Kb) |
| Abstract: | The phenomenon of mirage effect suffered by a He-Ne laser beam has been utilized to detect phase transitions in solids. It has been observed that anomalous fluctuations of large amplitude occur in the signal level near the transition temperature. The mean square value of the fluctuation is found to exhibit a well-defined peak at this point. Results of measurements made in the case of crystals of TGS ((NH2CH2COOH)3.H2SO4) and a ceramic sample (BaTiO3) are given to illustrate this technique. |
| URI: | http://dyuthi.cusat.ac.in/purl/2578 |
| Files | Size |
|---|---|
| Dyuthi-P0138.pdf | (219.7Kb) |
| Abstract: | We report on a laser induced photoacoustic study of the nematic-to-isotropic transition in certain commercial nematic liquid crystal mixtures, namely BL001, BL002, BL032 and BL035. A simple analysis of the experimental data using the Rosencwaig–Gersho theory shows that the heat capacities of all these compounds exhibit a sharp peak as the temperature of the sample is varied across the transition region. Also, substantial differences in the photoacoustic signal amplitudes in nematic and isotropic phases have been noticed for all the mixtures. The increased light scattering property of the nematic phase may be the reason for the enhanced photoacoustic signal amplitude in this phase. |
| URI: | http://dyuthi.cusat.ac.in/purl/1839 |
| Files | Size |
|---|---|
| Use of photoaco ... iquid crystal mixtures.pdf | (152.8Kb) |