Next PageAbstract: | The MgAl2O4 ceramics were prepared by the conventional solid-state ceramic route and the dielectric properties studied in the microwave frequency region (3–13 GHz). The phase purity and crystal structure were identified using the X-ray diffraction technique. The MgAl2O4 spinel ceramics show interesting microwave dielectric properties (εr = 8.75, Qux f = 68 900 GHz (loss tangent = 0.00017 at 12.3 GHz), τf =−75 ppm/◦C). The MgAl2O4 has high negative τf, which precludes its immediate use in practical applications. Hence the microwave dielectric properties of MgAl2O4 spinels were tailored by adding different mole fractions of TiO2. The εr and Q factor of the mixed phases were increased with the molar addition of TiO2 into the spinel to form mixtures based on (1−x)MgAl2O4-xTiO2 (x = 0.0−1.0). For x = 0.25 in (1−x)MgAl2O4-xTiO2, the microwave quality factor reaches a maximum value of Qux f = 105 400 GHz (loss tangent = 0.00007 at 7.5 GHz) where εr and τf are 11.035 and −12 ppm/◦C, respectively. The microwave dielectric properties of the newly developed 0.75MgAl2O4-0.25TiO2 dielectric is superior to several commercially available low loss dielectric substrates. |
URI: | http://dyuthi.cusat.ac.in/purl/519 |
Files | Size |
---|---|
APA3282.pdf | (689.8Kb) |
Abstract: | A new microwave dielectric resonator Ba(Tb1/2Nb1/2)03 has been prepared and characterized in the microwave frequency region. 1 wt% CeO2 is used as additive to reduce the sintering temperature. The sintered samples were characterized by XRD, SEM and Raman spectroscopic methods. Microwave DR properties such as er, Q factor and temperature-coefficient of resonant frequency (Ti) have been measured using a HP 8510 B Network Analyzer. Cylindrical DRs of Ba(Tb1/2Nbi/2)03 showed high Er (~ 37), high Q (~3,200) and low Tf (~10 ppm /°C) at 4 GHz and hence are useful for practical applications |
URI: | http://dyuthi.cusat.ac.in/purl/1447 |
Files | Size |
---|---|
Ba(Tb1 2Nb1 2)0 ... e dielectric resonator.PDF | (2.173Mb) |
Abstract: | The impedance bandwidth of a high permittivity cylindrical dielectric resonator antenna excited by a micro strip line was significantly improved by modifying the feed geometry. The 10 dB return loss bandwidth is enhanced from 12 to 26% without much affecting the gain and other radiation properties of the antenna. Good agreement has been observed between the predicted and measured results |
URI: | http://dyuthi.cusat.ac.in/purl/1579 |
Files | Size |
---|---|
Broadband cylin ... dified microstrip line.PDF | (1.018Mb) |
Abstract: | The impedance bandwidth of a high permittivity cylindrical dielectric resonator antenna excited by a micro strip line was significantly improved by modifying the feed geometry. The 10 dB return loss bandwidth is enhanced from 12 to 26% without much affecting the gain and other radiation properties of the antenna. Good agreement has been observed between the predicted and measured results |
URI: | http://dyuthi.cusat.ac.in/purl/1359 |
Files | Size |
---|---|
Broadband cylin ... dified microstrip line.PDF | (1.018Mb) |
Abstract: | very-high-permittivity (e, = 100) multiband dielectrice> e resonator antenna is presented. The compact antenna, excited by a m:'crostrip line, resonates at two frequencies centered around the 1.9- GHz and 2.4-GHz bands with identical polarization . The behavior of the antenna at different positions along the feed line is studied and optimized. Multiple resonances with the same polarization and broad radioticn patterns suggest the suitability of the antenna for multiband wireless application |
URI: | http://dyuthi.cusat.ac.in/purl/1404 |
Files | Size |
---|---|
A compact very- ... wireless applications.PDF | (1.327Mb) |
Abstract: | A new method for enhancing the 2.1 VSWR impedance bandwidth of microstrip antennas is presented. Bandwidth enhancement is achieved by loading the microstrip antenna by a ceramic microwave dielectric resonator (DR). The validity of this technique has been established using rectangular and circular radiating geometries. This method improves the bandwidth of a rectangular microstrip antenna to more than 10% (= 5 times that of a conventional rectangular microstrip antenna) with an enhanced gain of I dB |
URI: | http://dyuthi.cusat.ac.in/purl/1367 |
Files | Size |
---|---|
Dielecting-reso ... ndwidth and efficiency.PDF | (1.297Mb) |
Abstract: | Ceramic dielectrics with high dielectric constant in the microwave frequency range are used as filters, oscillators [I], etc. in microwave integrated circuits (MICs) particularly in modern communication systems like cellular telephones and satellite communications. Such ceramics, known as 'dielectric resonators (DRs),donot only offer miniaturisation and reduce the weight of the microwave components. but also improve the efficiency of MICs |
URI: | http://dyuthi.cusat.ac.in/purl/1437 |
Files | Size |
---|---|
Dielectric properties of Ba5Nb4O15 ceramic.PDF | (1.376Mb) |
Dielectric properties of Ba5Nb4O15 ceramic.PDF | (1.376Mb) |
Abstract: | The effect of dopants with different valencies and ionic radii on the densification, structural ordering, and microwave dielectric properties of Ba(Mg1t3Tazt3)O3 (BMT) is investigated. It is found that dopants such as Sb,05, MnO, ZrO,, WO1, and ZnO improve the microwave dielectric properties of BMT. Addition of trivalent dopants is detrimental to the cation ordering and dielectric properties of BMT. A correlation between the microwave dielectric properties of BMT and ionic radii of the dopant has been established. The variation of the dielectric properties of pure and doped BMT at cryogenic temperatures is also discussed |
URI: | http://dyuthi.cusat.ac.in/purl/1489 |
Files | Size |
---|---|
The effect of d ... o.33Ta0.67)03 ceramics.PDF | (5.114Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/1491 |
Files | Size |
---|---|
Effect of Nonst ... of Ba(Mgo.33Tao.67)03.PDF | (6.590Mb) |
Abstract: | The effect of glass additives on the densification , phase evolution, microstructure and microwave dielectric properties of Ba(Mg1;3 Ta2i3)03 (BMT) was investigated . Different weight percentages of quenched glass such as B203 , Si02, B203-SiO2, ZnO-B203, 5ZnO-2B2O3, Al203-SiO2, Na20-2B203.10H20, BaO-B203-SiO2, MgO-B203-SiO2, PbO-B203-SiO2 , ZnO-B203-SiO2 and 2MgO-Al203-5SiO2 were added to calcined BMT precursor . The sintering temperature of the glass -added BMT samples were lowered down to 1300 °C compared to solid-state sintering where the temperature was 1650 °C. The formation of high temperature satellite phases such as Ba5Ta4O15 and Ba7Ta6O22 were found to be suppressed by the glass addition . Addition of glass systems such as B203, ZnO-B203, 5ZnO-2B203 and ZnO-B203-SiO2 improved the densification and microwave dielectric properties. Other glasses were found to react with BMT to form low-Q phases which prevented densification . The microwave dielectric properties of undoped BMT with a densification of 93 . 1 % of the theoretical density were Cr = 24 . 8, Tr = 8 ppm/°C and Q„ x f= 80,000 GHz. The BMT doped with 1.0 wt% of B203 has Q„ x f = 124,700GHz, Cr = 24.2, and T f = -1.3 ppm /°C. The unloaded Q factor of 0.2 wt% ZnO-B203-doped BMT was 136,500 GHz while that of 1.0 wt% of 5ZnO-2B203 added ceramic was Q„ x f= 141,800 GHz . The best microwave quality factor was observed for ZnO -B203-SiO2 (ZBS) glass-added ceramics which can act as a perfect liquid-phase medium for the sintering of BMT. The microwave dielectric properties of 0.2wt% ZBS-added BMT dielectric was Q„ x f= 152,800 GHz, F,= 25.5, and Tr = - 1.5 ppm/°C |
URI: | http://dyuthi.cusat.ac.in/purl/1495 |
Files | Size |
---|---|
Effect of Nonst ... of Ba(Mgo.33Tao.67)03.PDF | (6.590Mb) |
Abstract: | A novel technique fitr the bat dividth enhancement of conventional rectangular microstrip antenna is proposed in this paper. When a high permittivity dielectric resonator of suitable resonant frequency was loaded over the patch. the % bandwidth of the antenna was increased by more than five tunes without much affecting its gain and radiation performance. A much more improved bandwidth was obtained when the dielectric resonator was placed on the feedline. Experimental study shows a 2:1 VSWR bandwidth of more than 10% and excellent cross polarization performance with increased pass band and radiation coverage abnost the same as that of rectangular microstrip antenna |
URI: | http://dyuthi.cusat.ac.in/purl/1389 |
Files | Size |
---|---|
Enhanced bandwi ... dielectric resonators.PDF | (1.874Mb) |
Abstract: | A new group of compounds with composition (Ba5-xSrx) Nb4015, having high permittivity and low loss have been prepared and characterized in the microwave frequency region . X-ray diffraction studies showed that monophase compound existed for all values of x from 0 to 5. Microwave dielectric properties such as and c f showed smooth variation with x , while the unloaded quality factor (Qu) showed remarkable improvement with x |
URI: | http://dyuthi.cusat.ac.in/purl/1440 |
Files | Size |
---|---|
Sreemoolanadhan,H & Sebastian,M.T.PDF | (1.655Mb) |
Abstract: | In this paper, the advantages of using L-shaped microviij) feed to e.tcite a rectangular dielectric resonator cuuenna (DRA) by elemanagnetic coupling are presented. This feeding technique enhances the hardsvidth and gain of the antenna without affecting its size. The experimental re srdts are validated using Fidelity software based on the finitedifference tine-domain (FDTD) method |
URI: | http://dyuthi.cusat.ac.in/purl/1425 |
Files | Size |
---|---|
L-strip-fed wid ... tric resonator antenna.PDF | (932.7Kb) |
Abstract: | A microwave dielectric ceramic resonator based on BaCe2Ti5O15 and Ba5Nb4O15 have been prepared by conventional solid state ceramic route. The dielectric resonators (DRs) have high dielectric constant 32 and 40 for BaCe2Ti5O15 and Ba5Nb4O15, respectively. The whispering gallery mode (WGM) technique was employed for the accurate determination of the dielectric properties in the microwave frequency range. The BaCe2Ti5O15 and Ba5Nb4O15 have quality factors (Q X F) of 30,600 and 53,000 respectively. The quality factor is found to depend on the azimuthal mode numbers. The temperature coefficient of resonant frequency (Tr) of BaCe2Ti5O15 and Ba5Nb4O15 have been measured accurately using different resonant modes and are + 41 and + 78 ppm/K, respectively |
URI: | http://dyuthi.cusat.ac.in/purl/1446 |
Files | Size |
---|---|
Microwave chara ... ng gallery mode method.PDF | (2.989Mb) |
Abstract: | The microwave dielectric properties of (I -x)CaTiO3-xSm(Mg1/2Tit,2)O3(0.1 <-x< 1.0) have been investigated. The system forms a solid solution throughout the entire compositional range. The dielectric constant decreases from 86 to 25 as x varies from 0.1 to 1.0. The Qxf varies non-linearly and increases for composition with x> 0.6. The nonmonotonic variation with composition x is more pronounced in Tt than in er. The microwave dielectric properties indicate the possibility of a phase transformation for x between 0.4 and 0.5 |
URI: | http://dyuthi.cusat.ac.in/purl/1453 |
Files | Size |
---|---|
Microwave diele ... 3 [0. 1 _x 1] ceramics.PDF | (2.946Mb) |
Abstract: | microwave dielectric properties of ceramics based on Ba(Mgv3Ta(2-2x)t3W,t3Tixt3)O3 is investigated as a function of x. The 15 densification as well as dielectric properties deteriorate with increase in the substitution levels of (Ti 1,3W113)333 + at (Ta213)3.33+ site 16 in Ba(Mg113Ta213)03. The rt is approaching zero between x = 0.1 and 0.15 in Ba(Mg it3Ta(2-2,,.)t3W,it3Ti,Tt3)O3 where quality factor is 17 reasonably good (Qu x f = 80,000-90,000 GHz). The Ba(Mg1,3Ta(2_,013W,13Ti,,13)03 with x = 1.0 has e, = 15.4, rf= -25.1 ppm/ 18 "C, Q„ x f = 35,400 GHz |
URI: | http://dyuthi.cusat.ac.in/purl/1488 |
Files | Size |
---|---|
Microwave diele ... 3Wx3Tixf3) 03 ceramics.PDF | (3.228Mb) |
Abstract: | The BaO-2CeO2-nTiO2 ceramics with n = 3, 4 and 5 have been prepared with CeO2 as starting material . The ceramics have been characterized using scanning electron microscopy , X-ray diffraction , Raman and X-ray photoelectron spectroscopy techniques. The microwave dielectric properties have been measured using standard dielectric resonator techniques . BaO-2CeO2-3TiO2 (123), BaO-2CeO2-4TiO2 ( 124) and BaO-2CeO2-5TiO2 ( 125) ceramics showed dielectric constants of 38, 27 and 32, respectively . All the ceramics showed fairly good unloaded Q - factors . 124 and 125 compounds exhibited low tf values, while 123 showed a high rf value |
URI: | http://dyuthi.cusat.ac.in/purl/1493 |
Files | Size |
---|---|
Microwave diele ... -2CeO2-nTiO2 ceramics.PDF | (3.306Mb) |
Abstract: | Dielectric resonator ceramics with composition formula Ba[(D3+0.3 Bi0.2)Nb0.5]O3,where D3+=Y,Pr,Sm,Gd,Dy and Er,were prepared by the conventional ceramic preparation route |
URI: | http://dyuthi.cusat.ac.in/purl/1441 |
Files | Size |
---|---|
Microwave diele ... Y, Pr, Sm, Gd, Dy, Er).PDF | (2.529Mb) |
Abstract: | New dielectric ceramics with formula BaTi3Nb4, O„ and Ba6Til4Nbz039 have been prepared and characterized. BaTi3Nba017 was densified to 92% of TD after firing at 1310 oC for 4 h. However, Ba6Ti 1 4Nb2O39 fired under optimized conditions (1260 ` C for 4 h) showed only 85% TD together with secondary phase. The crystal system of both of the compositions is orthorhombic |
URI: | http://dyuthi.cusat.ac.in/purl/1443 |
Files | Size |
---|---|
New high permit ... TiO2-Nb2O5 composition.PDF | (2.094Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/1801 |
Files | Size |
---|---|
Photoacoustic i ... f excess lead oxide on.pdf | (40.30Kb) |
Now showing items 1-20 of 34
Next PageDyuthi Digital Repository Copyright © 2007-2011 Cochin University of Science and Technology. Items in Dyuthi are protected by copyright, with all rights reserved, unless otherwise indicated.