Now showing items 1-8 of 8
| Abstract: | The MgAl2O4 ceramics were prepared by the conventional solid-state ceramic route and the dielectric properties studied in the microwave frequency region (3–13 GHz). The phase purity and crystal structure were identified using the X-ray diffraction technique. The MgAl2O4 spinel ceramics show interesting microwave dielectric properties (εr = 8.75, Qux f = 68 900 GHz (loss tangent = 0.00017 at 12.3 GHz), τf =−75 ppm/◦C). The MgAl2O4 has high negative τf, which precludes its immediate use in practical applications. Hence the microwave dielectric properties of MgAl2O4 spinels were tailored by adding different mole fractions of TiO2. The εr and Q factor of the mixed phases were increased with the molar addition of TiO2 into the spinel to form mixtures based on (1−x)MgAl2O4-xTiO2 (x = 0.0−1.0). For x = 0.25 in (1−x)MgAl2O4-xTiO2, the microwave quality factor reaches a maximum value of Qux f = 105 400 GHz (loss tangent = 0.00007 at 7.5 GHz) where εr and τf are 11.035 and −12 ppm/◦C, respectively. The microwave dielectric properties of the newly developed 0.75MgAl2O4-0.25TiO2 dielectric is superior to several commercially available low loss dielectric substrates. |
| URI: | http://dyuthi.cusat.ac.in/purl/519 |
| Files | Size |
|---|---|
| APA3282.pdf | (689.8Kb) |
| Abstract: | The effect of dopants with different valencies and ionic radii on the densification, structural ordering, and microwave dielectric properties of Ba(Mg1t3Tazt3)O3 (BMT) is investigated. It is found that dopants such as Sb,05, MnO, ZrO,, WO1, and ZnO improve the microwave dielectric properties of BMT. Addition of trivalent dopants is detrimental to the cation ordering and dielectric properties of BMT. A correlation between the microwave dielectric properties of BMT and ionic radii of the dopant has been established. The variation of the dielectric properties of pure and doped BMT at cryogenic temperatures is also discussed |
| URI: | http://dyuthi.cusat.ac.in/purl/1489 |
| Files | Size |
|---|---|
| The effect of d ... o.33Ta0.67)03 ceramics.PDF | (5.114Mb) |
| URI: | http://dyuthi.cusat.ac.in/purl/1491 |
| Files | Size |
|---|---|
| Effect of Nonst ... of Ba(Mgo.33Tao.67)03.PDF | (6.590Mb) |
| Abstract: | The effect of glass additives on the densification , phase evolution, microstructure and microwave dielectric properties of Ba(Mg1;3 Ta2i3)03 (BMT) was investigated . Different weight percentages of quenched glass such as B203 , Si02, B203-SiO2, ZnO-B203, 5ZnO-2B2O3, Al203-SiO2, Na20-2B203.10H20, BaO-B203-SiO2, MgO-B203-SiO2, PbO-B203-SiO2 , ZnO-B203-SiO2 and 2MgO-Al203-5SiO2 were added to calcined BMT precursor . The sintering temperature of the glass -added BMT samples were lowered down to 1300 °C compared to solid-state sintering where the temperature was 1650 °C. The formation of high temperature satellite phases such as Ba5Ta4O15 and Ba7Ta6O22 were found to be suppressed by the glass addition . Addition of glass systems such as B203, ZnO-B203, 5ZnO-2B203 and ZnO-B203-SiO2 improved the densification and microwave dielectric properties. Other glasses were found to react with BMT to form low-Q phases which prevented densification . The microwave dielectric properties of undoped BMT with a densification of 93 . 1 % of the theoretical density were Cr = 24 . 8, Tr = 8 ppm/°C and Q„ x f= 80,000 GHz. The BMT doped with 1.0 wt% of B203 has Q„ x f = 124,700GHz, Cr = 24.2, and T f = -1.3 ppm /°C. The unloaded Q factor of 0.2 wt% ZnO-B203-doped BMT was 136,500 GHz while that of 1.0 wt% of 5ZnO-2B203 added ceramic was Q„ x f= 141,800 GHz . The best microwave quality factor was observed for ZnO -B203-SiO2 (ZBS) glass-added ceramics which can act as a perfect liquid-phase medium for the sintering of BMT. The microwave dielectric properties of 0.2wt% ZBS-added BMT dielectric was Q„ x f= 152,800 GHz, F,= 25.5, and Tr = - 1.5 ppm/°C |
| URI: | http://dyuthi.cusat.ac.in/purl/1495 |
| Files | Size |
|---|---|
| Effect of Nonst ... of Ba(Mgo.33Tao.67)03.PDF | (6.590Mb) |
| Abstract: | microwave dielectric properties of ceramics based on Ba(Mgv3Ta(2-2x)t3W,t3Tixt3)O3 is investigated as a function of x. The 15 densification as well as dielectric properties deteriorate with increase in the substitution levels of (Ti 1,3W113)333 + at (Ta213)3.33+ site 16 in Ba(Mg113Ta213)03. The rt is approaching zero between x = 0.1 and 0.15 in Ba(Mg it3Ta(2-2,,.)t3W,it3Ti,Tt3)O3 where quality factor is 17 reasonably good (Qu x f = 80,000-90,000 GHz). The Ba(Mg1,3Ta(2_,013W,13Ti,,13)03 with x = 1.0 has e, = 15.4, rf= -25.1 ppm/ 18 "C, Q„ x f = 35,400 GHz |
| URI: | http://dyuthi.cusat.ac.in/purl/1488 |
| Files | Size |
|---|---|
| Microwave diele ... 3Wx3Tixf3) 03 ceramics.PDF | (3.228Mb) |
| Abstract: | Dielectric ceramics based on solid solution phases of [RE1_x= REr]TiNb06, where REI_s = Nd, Pr, Sm and RE' = Dy, Gd and Y, were prepared by the conventional solid-state ceramic route for values of x. The ceramic samples are characterized by X-ray diffraction and microwave methods. Ceramics based on RE (Pr, Nd and Sm) belonging to aeschynite group shows positive value of Tf and those based on RE (Gd, Dy and Y) belonging to euxenite group show negative value of r f. The solid solution phases between the aeschynite and the euxenite group shows intermediate dielectric constant and r f values. The results indicate the possibility of tailoring the dielectric properties by varying the composition of the solid solution phases. The range of solid solubility of euxenite in aeschenite and aeschenite in euxenite are different for different rare earth ions |
| URI: | http://dyuthi.cusat.ac.in/purl/1449 |
| Files | Size |
|---|---|
| Synthesis , cha ... 06 dielectric ceramics.PDF | (1.260Mb) |
| Abstract: | Microwave dielectric ceramics based on GdTiNb,-,.Ta,O6 and Sml _.,Y,TiTa06 have been prepared by conventional solid state method . The GdTiTaO6 and SmTiTaO6 have aeschenite structure with positive rr and GdTiNbO6 and YTiTaO6 have euxenite structure with negative rr. The rr of the ceramics has been tuned by preparing solid solution phases between the aeschynites and euxenites for a possible zero rr material . It is observed that GdTiNbt_YTa.,O6 undergoes a phase transition from aeschynite to euxenite when x=0.75 and in Sml-,YxTiTa06 for x= 0.73. The microwave dielectric properties change abruptly near the transition region . The rr value approaches zero near the phase transition region while the samples have poor sinterability and poor quality factor . The unloaded quality factor, dielectric constant and the sign of rr of the solid solution phases are found to depend on the average ionic radius of the rare earth ion in RE ,-5RE',TiTaO6. The boundary of the euxenite-aeschynite phase transition occurs at an average ( RE) ionic radius of 0.915 A in Sm,_, Y,.TiTaO6 solid solution phases |
| URI: | http://dyuthi.cusat.ac.in/purl/1455 |
| Files | Size |
|---|---|
| Tailoring the m ... 1 _X Y,TiTa06 ceramics.PDF | (3.705Mb) |
| Abstract: | The microwave dielectric properties of ZnAl2O4 spinels were investigated and their properties were tailored by adding different mole fractions of Ti02. The samples were synthesized using the mixed oxide rout.e. The phase purity and crystal structure were identified using X-ray diffraction technique. The sintered specimens were characterized in the microwave frequency range (3-13 GHz). The ZnA12O4 ceramics exhibited interesting dielectric properties (dielectric constant (e,.) = 8.5, unloaded quality factor (Q.) = 4590 at 12.27 GHz and temperature coefficient of resonant frequency (Tf) = -79 ppm/°C). Addition of Ti02 into the spinel improved its properties and the Tf approached zero for 0.83ZnAl2O4- 0.17TiO2• This temperature compensated composition has excellent microwave dielectric properties (Cr _ 12.67, Q, = 9950 at 10.075 GHz) which can be exploited for microwave substrate applications |
| URI: | http://dyuthi.cusat.ac.in/purl/1492 |
| Files | Size |
|---|---|
| Temperature sta ... substrate applications.PDF | (3.226Mb) |
Now showing items 1-8 of 8