Abstract: | Ferrofluids belonging to the series NixFe1 xFe2O4 were synthesised by two different procedures—one by standard co-precipitation techniques, the other by co-precipitation for synthesis of particles and dispersion aided by high-energy ball milling with a view to understand the effect of strain and size anisotropy on the magneto-optical properties of ferrofluids. The birefringence measurements were carried out using a standard ellipsometer. The birefringence signal obtained for chemically synthesised samples was satisfactorily fitted to the standard second Langevin function. The ball-milled ferrofluids showed a deviation and their birefringence was enhanced by an order. This large enhancement in the birefringence value cannot be attributed to the increase in grain size of the samples, considering that the grain sizes of sample synthesised by both modes are comparable; instead, it can be attributed to the lattice strain-induced shape anisotropy(oblation) arising from the high-energy ball-milling process. Thus magnetic-optical (MO) signals can be tuned by ball-milling process, which can find potential applications. |
URI: | http://dyuthi.cusat.ac.in/purl/2831 |
Files | Size |
---|---|
Dyuthi-P00387.pdf | (291.1Kb) |
Abstract: | ZnO nanoflowers were synthesized by the hydrothermal process at an optimized growth temperature of 200 ◦C and a growth/reaction time of 3 h. As-prepared ZnO nanoflowers were characterized by x-ray diffraction, scanning electron microscopy, UV–visible and Raman spectroscopy. X-ray diffraction and Raman studies reveal that the as-synthesized flower-like ZnO nanostructures are highly crystalline with a hexagonal wurtzite phase preferentially oriented along the (1 0 1 1) plane. The average length (234–347 nm) and diameter (77–106 nm) of the nanorods constituting the flower-like structure are estimated using scanning electron microscopy studies. The band gap of ZnO nanoflowers is estimated as 3.23 eV, the lowering of band gap is attributed to the flower-like surface morphology and microstructure of ZnO. Room temperature photoluminescence spectrum shows a strong UV emission peak at 392 nm, with a suppressed visible emission related to the defect states, indicating the defect free formation of ZnO nanoflowers that can be potentially used for UV light-emitting devices. The suppressed Raman bands at 541 and 583 cm−1 related to defect states in ZnO confirms that the ZnO nanoflowers here obtained have a reduced presence of defects |
Description: | J. Phys. D: Appl. Phys. 45 (2012) 425103 (6pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4555 |
Files | Size |
---|---|
Enhanced UV emi ... e hydrothermal process.pdf | (601.8Kb) |
Abstract: | The differaction efficiency,sensitivity and storage life of Methylene Blue sencitized poly (vinyl chloride) film was improved by the addition of an electron donor in the matrix. The addition of pyridine enhanced the diffraction efficiency by two times and storage life of the gratings was increased to 2-3 days. |
URI: | http://dyuthi.cusat.ac.in/purl/608 |
Files | Size |
---|---|
enhancement of DE by electron donor.pdf | (329.4Kb) |
Abstract: | The effect of frequency, composition and temperature on the a.c. electrical conductivity were studied for the ceramic, Ni1–xZnxFe2O4, as well as the filler (Ni1–xZnxFe2O4) incorporated rubber ferrite composites (RFCs). Ni1–xZnxFe2O4 (where x varies from 0 to 1 in steps of 0×2) were prepared by usual ceramic techniques. They were then incorporated into a butyl rubber matrix according to a specific recipe. The a.c. electrical conductivity (sa.c.) calculations were carried out by using the data available from dielectric measurements and by employing a simple relationship. The a.c. conductivity values were found to be of the order of 10–3 S/m. Analysis of the results shows that sa.c. increases with increase of frequency and the change is same for both ceramic Ni1–xZnxFe2O4 and RFCs. sa.c. increases initially with the increase of zinc content and then decreases with increase of zinc. Same behaviour is observed for RFCs too. The dependence of sa.c. on the volume fraction of the magnetic filler was also studied and it was found that the a.c. conductivity of RFCs increases with increase of volume fraction of the magnetic filler. Temperature dependence of conductivity was studied for both ceramic and rubber ferrite composites. Conductivity shows a linear dependence with temperature in the case of ceramic samples |
Description: | Bull. Mater. Sci., Vol. 25, No. 7, December 2002, pp. 599–607 |
URI: | http://dyuthi.cusat.ac.in/purl/4355 |
Files | Size |
---|---|
Evaluation of a ... ielectric measurements.pdf | (232.7Kb) |
Abstract: | Superparamagnetic nanocomposites based on Y-Fe2O3 and sulphonated polystyrene were synthesised by ion-exchange process and the structural characterisation has been carried out using X-ray diffraction technique. Doping of cobalt in to the Y-Fe2O3 lattice was effected in situ and the doping was varied in the atomic percentage range 1–10. The optical absorption studies show a band gap of 2.84 eV, which is blue shifted by 0.64 eV when compared to the reported values for the bulk samples (2.2 eV). This is explained on the basis of weak quantum confinement. Further size reduction can result in a strong confinement, which can yield transparent magnetic nanocomposites because of further blue shifting. The band gap gets red shifted further with the addition of cobalt in the lattice and this red shift increases with the increase in doping. The observed red shift can be attributed to the strain in the lattice caused by the anisotropy induced by the addition of cobalt. Thus, tuning of bandgap and blue shifting is aided by weak exciton confinement and further red shifting of the bandgap is assisted by cobalt doping. |
URI: | http://dyuthi.cusat.ac.in/purl/2836 |
Files | Size |
---|---|
Dyuthi-P00392.pdf | (199.0Kb) |
Abstract: | Nanoparticles are of immense importance both from the fundamental and application points of view. They exhibit quantum size effects which are manifested in their improved magnetic and electric properties. Mechanical attrition by high energy ball milling (HEBM) is a top down process for producing fine particles. However, fineness is associated with high surface area and hence is prone to oxidation which has a detrimental effect on the useful properties of these materials. Passivation of nanoparticles is known to inhibit surface oxidation. At the same time, coating polymer film on inorganic materials modifies the surface properties drastically. In this work a modified set-up consisting of an RF plasma polymerization technique is employed to coat a thin layer of a polymer film on Fe nanoparticles produced by HEBM. Ball-milled particles having different particle size ranges are coated with polyaniline. Their electrical properties are investigated by measuring the dc conductivity in the temperature range 10–300 K. The low temperature dc conductivity (I–V ) exhibited nonlinearity. This nonlinearity observed is explained on the basis of the critical path model. There is clear-cut evidence for the occurrence of intergranular tunnelling. The results are presented here in this paper |
Description: | Nanotechnology 17 (2006) 4765–4772 |
URI: | http://dyuthi.cusat.ac.in/purl/4381 |
Files | Size |
---|---|
Evidence for in ... ted α-Fe nanoparticles.pdf | (762.3Kb) |
Abstract: | Nanoparticles of manganese ferrite were prepared by the chemical co-precipitation technique. The dielectric parameters, namely, real and imaginary dielectric permittivity (ε and ε ), ac conductivity (σac) and dielectric loss tangent (tan δ), were measured in the frequency range of 100 kHz–8MHz at different temperatures. The variations of dielectric dispersion (ε ) and dielectric absorption (ε ) with frequency and temperature were also investigated. The variation of dielectric permittivity with frequency and temperature followed the Maxwell–Wagner model based on interfacial polarization in consonance with Koops phenomenological theory. The dielectric loss tangent and hence ε exhibited a relaxation at certain frequencies and at relatively higher temperatures. The dispersion of dielectric permittivity and broadening of the dielectric absorption suggest the possibility of a distribution of relaxation time and the existence of multiple equilibrium states in manganese ferrite. The activation energy estimated from the dielectric relaxation is found to be high and is characteristic of polaron conduction in the nanosized manganese ferrite. The ac conductivity followed a power law dependence σac = Bωn typical of charge transport assisted by a hopping or tunnelling process. The observed minimum in the temperature dependence of the frequency exponent n strongly suggests that tunnelling of the large polarons is the dominant transport process |
Description: | J. Phys. D: Appl. Phys. 41 (2008) 185005 (9pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4354 |
Files | Size |
---|---|
Evidence for po ... ured manganese ferrite.pdf | (2.000Mb) |
Abstract: | In any investigation, information about the molecules under consideration is very essential for tailoring their properties. Evaluation of dispersion parameters, namely optical dielectric constant, static dielectric constant, relaxation time and spreading factor, assumes significance in this context. Dielectric spectroscopy is a useful tool for estimating these parameters. Not only does it reveal details about these constants but it also gives insight into the mechanism of conduction. In this paper the evaluation of dispersion parameters of cobalt phthalocyanine tetramer in the temperature range 300–393K is attempted using Cole–Cole plots. The temperature variation of the spreading factor indicates the existence of multiple equilibrium positions in the case of cobalt phthalocyanine tetramer. To the best of our knowledge, the evaluation of dispersion parameters for cobalt phthalocyanine tetramer is reported for the first time |
Description: | J. Phys. D: Appl. Phys. 39 (2006) 1678–1683 |
URI: | http://dyuthi.cusat.ac.in/purl/4409 |
Files | Size |
---|---|
Evidence for th ... ielectric spectroscopy.pdf | (274.5Kb) |
Abstract: | Ultra thin films based on CoFe were prepared from a composite target employing thermal evaporation. The microstructure of the films was modified by thermal annealing. The relationship between microstructure and magnetic properties of the films was investigated using techniques like glancing angle X-ray diffraction (GXRD), transmission electron microscopy (TEM) and vibrating sample magnetometry (VSM). The GXRD and TEM investigations showed an onset of crystallization of CoFe at around 373 K. The magnetic softness of the films improved with thermal annealing but at higher annealing temperature it is found to be deteriorating. Annealing inducedmodification of surface morphology of the alloy thin filmswas probed by atomic force microscopy (AFM). Surface smoothening was observed with thermal annealing and the observed magnetic properties correlate well with surface modifications induced by thermal annealing |
Description: | Surface & Coatings Technology 236 (2013) 246–251 |
URI: | http://dyuthi.cusat.ac.in/purl/4429 |
Files | Size |
---|---|
Evolution of st ... with thermal annealing.pdf | (1.310Mb) |
Abstract: | The magnetic properties of amorphous Fe–Ni–B based metallic glass nanostructures were investigated. The nanostructures underwent a spin-glass transition at temperatures below 100 K and revealed an irreversible temperature following the linear de Almeida–Thouless dependence. When the nanostructures were cooled below 25 K in a magnetic field, they exhibited an exchange bias effect with enhanced coercivity. The observed onset of exchange bias is associated with the coexistence of the spin-glass phase along with the appearance of another spin-glass phase formed by oxidation of the structurally disordered surface layer, displaying a distinct training effect and cooling field dependence. The latter showed a maximum in exchange bias field and coercivity, which is probably due to competing multiple equivalent spin configurations at the boundary between the two spin-glass phases |
Description: | J. Phys.: Condens. Matter 24 (2012) 256004 (8pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4413 |
Files | Size |
---|---|
Exchange bias e ... B based metallic glass.pdf | (1.716Mb) |
Abstract: | A methylene-blue-sensitized polymer blend of polyvinyl alcohol and polyacrylic acid is fabricated and tested for holographic recording. It was found to have good characteristics such as high sensitivity, storage stability, ease of fabrication, and environmental stability. Optimization of the ratio of polyvinyl alcohol polyacrylic acid, the sensitizer concentration, pH, energy, diffraction efficiency measurements, etc., have been done. pH is found to have a great influence on the recovery of the dye in this matrix. The results of experimental investigations into the properties of this new material are reported. |
URI: | http://dyuthi.cusat.ac.in/purl/609 |
Files | Size |
---|---|
Fabrication and characterization .pdf | (293.8Kb) |
Abstract: | Two-dimensional electronic systems play a crucial role in modern electronics and offer a multitude of opportunities to study the fundamental phenomena at low dimensional physics. A quantum well heterostructure based on polyaniline (P) and iodine doped polyaniline (I) thin films were fabricated using radio frequency plasma polymerization on indium tin oxide coated glass plate. Scanning probe microscopy and scanning electron microscopy studies were employed to study the morphology and roughness of the polymer thin films. Local electronic density of states (LDOS) of the P–I–P heterostructures is probed using scanning tunnelling spectroscopy (STS). A step like LDOS is observed in the P–I–P heterostructure and is attributed to the quantum well confinement of electrons in the polymer heterostructure. |
Description: | J. Phys. D: Appl. Phys. 42 (2009) 165309 (7pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4416 |
Files | Size |
---|---|
Fabrication of ... erized aniline and its.pdf | (853.9Kb) |
Abstract: | Ferrofluids belonging to the series, Ni x Fe1-x Fe2O4 and Zn x Fe1-x Fe2O4, were synthesized using cold co-precipitation. Liquid films of these ferrofluids were prepared by encapsulating the ferrofluids in between two optically smooth and ultrasonically cleaned glass plates. Magnetic field induced laser transmission through these ferrofluid films has been investigated. Magnetic field values can be calibrated in terms of output laser power in the low field region in which the variation is linear. This set up can be used as a cheap optical gaussmeter in the low field regime. Using the same set-up, the saturation magnetization of the sample used can also be calculated with a sample that is pre-characterized. Hence both magnetization of the sample, as well as applied magnetic field can be sensed and calculated with a precalibrated sample. |
URI: | http://dyuthi.cusat.ac.in/purl/2844 |
Files | Size |
---|---|
Dyuthi-P00397.pdf | (176.9Kb) |
Abstract: | Fine particles of cobalt ferrite were synthesized by the sol–gel method. Subsequent heat treatment at different temperatures yielded cobalt ferrites having different grain sizes. X-ray diffraction studies were carried out to elucidate the structure of all the samples. Dielectric permittivity and ac conductivity of all the samples were evaluated as a function of frequency, temperature and grain size. The variation of permittivity and ac conductivity with frequency reveals that the dispersion is due to Maxwell–Wagner type interfacial polarization in general, with a noted variation from the expected behaviour for the cold synthesized samples. High permittivity and conductivity for small grains were explained on the basis of the correlated barrier-hopping model |
Description: | J. Phys. D: Appl. Phys. 40 (2007) 1593–1602 |
URI: | http://dyuthi.cusat.ac.in/purl/4350 |
Files | Size |
---|---|
Finite size eff ... e polarization effects.pdf | (975.7Kb) |
Abstract: | Nanoparticles of nickel ferrite have been synthesized by the sol–gel method and the effect of grain size on its structural and magnetic properties have been studied in detail. X-ray diffraction (XRD) studies revealed that all the samples are single phasic possessing the inverse spinel structure. Grain size of the sol–gel synthesized powders has been determined from the XRD data and the strain graph. A grain size of 9 nm was observed for the as prepared powders of NiFe2O4 obtained through the sol–gel method. It was also observed that strain was induced during the firing process. Magnetization measurements have been carried out on all the samples prepared in the present series. It was found that the specific magnetization of the nanosized NiFe2O4 powders was lower than that of the corresponding coarse-grained counterparts and decreased with a decrease in grain size. The coercivity of the sol–gel synthesized NiFe2O4 nanoparticles attained a maximum value when the grain size was 15nm and then decreased as the grain size was increased further. |
Description: | Journal of Magnetism and Magnetic Materials 302 (2006) 190–195 |
URI: | http://dyuthi.cusat.ac.in/purl/4347 |
Files | Size |
---|---|
Finite size eff ... esized NiFe2O4 powders.pdf | (265.1Kb) |
Abstract: | Flexile single layer electromagnetic wave absorbers were designed by incorporating appropriate amounts of carbon black in a nitrile butadiene rubber matrix along with an optimized amount of magnetic counterpart, namely, barium hexaferrite for applications in S, C, and X-bands. Effective dielectric permittivity and magnetic permeability were measured using cavity perturbation method in the frequency range of 2–12 GHz. The microwave absorbing characteristics of the composites were studied in the S, C, and X-bands employing a model in which an electromagnetic wave is incident normally on a metal terminated single layer. Reflection loss exceeding 20 dB is obtained for all the samples in a wide frequency range of 2–12 GHz when an appropriate absorber thickness between 5 and 9mm is chosen. The impact of carbon black is clearly observed in the optimized composites on the mechanical strength, thickness, band width of absorption, dielectric properties, |
Description: | J. Appl. Phys. 116, 024902 (2014) |
URI: | http://dyuthi.cusat.ac.in/purl/4426 |
Files | Size |
---|---|
Flexible microw ... 2–12 GHz applications.pdf | (2.341Mb) |
Abstract: | Multimodal imaging agents that combine magnetic and fluorescent imaging capabilities are desirable for the high spatial and temporal resolution. In the present work, we report the synthesis of multifunctional fluorescent ferrofluids using iron oxide as the magnetic core and rhodamine B as fluorochrome shell. The core–shell structure was designed in such a way that fluorescence quenching due to the inner magnetic core was minimized by an intermediate layer of silica. The intermediate passive layer of silica was realized by a novel method which involves the esterification reaction between the epoxy group of prehydrolysed 3-Glyidoxypropyltrimethoxysilane and the surfactant over iron oxide. The as-synthesized ferrofluids have a high saturation magnetization in the range of 62–65 emu/g and were found to emit light of wavelength 640 nm ( excitation = 446 nm). Time resolved life time decay analysis showed a bi-exponential decay pattern with an increase in the decay life time in the presence of intermediate silica layer. Cytotoxicity studies confirmed the cell viability of these materials. The in vitro MRI imaging illustrated a high contrast when these multimodal nano probes were employed and the R2 relaxivity of these ∗Author to whom correspondence should be addressed. Email: smissmis@gmail.com sample was found to be 334 mM−1s−1 which reveals its high potential as a T2 contrast enhancing agent |
Description: | Material Express, Vol. 2, No. 4, 2012 |
URI: | http://dyuthi.cusat.ac.in/purl/4400 |
Files | Size |
---|---|
Fluorescent Sup ... imodalCellular Imaging.pdf | (7.439Mb) |
Abstract: | Transition metal acetylides, MC2 (M=Fe, Co and Ni), exhibit ferromagnetic behavior of which TC is characteristic of their size and structure. CoC2 synthesized in anhydrous condition exhibited cubic structure with disordered C2− 2 orientation. Once being exposed to water (or air), the particles behave ferromagnetically due to the lengthening of the Co–Co distance by the coordination of water molecules to Co2+ cations. Heating of these particles induces segregation of metallic cores with carbon mantles. Electron beam or 193 nm laser beam can produce nanoparticles with metallic cores covered with carbon mantles |
Description: | Eur. Phys. J. D 34, 219–222 (2005) |
URI: | http://dyuthi.cusat.ac.in/purl/4550 |
Files | Size |
---|---|
Formation of ca ... ctron beam irradiation.pdf | (272.6Kb) |
Abstract: | FT-Raman and FT-IR spectra of ASnFe(PO4)3 [A=Na2, Ca, Cd] were recorded and analyzed. The bands were assigned in terms of the vibrational group frequencies of SnO6 octahedral and PO4 tetrahedral. The spectral analysis shows that the symmetry of corner shared octahedral (SnO6) and the tetrahedral (PO4) are lowered from their free ion symmetry state. The presence of Fe3+ ions disrupts the S–N–O–S–N chain in the structure. This causes distortion of SnO6 and PO4 in the structure of all the compounds. Also it is seen that there are two distinct PO4 tetrahedra of different P–O bond lengths. One of these tetrahedra is linearly distorted in all the title compounds. The PO4 frequencies and bond lengths are calculated theoretically and are in agreement with the experimental values. The presence of PO4 polyanion in the structure can reduce the redox energy and hence reduce the metal oxygen covalency strength in the structure |
Description: | Spectrochimica Acta Part A 78 (2011) 415–419 |
URI: | http://dyuthi.cusat.ac.in/purl/4556 |
Files | Size |
---|---|
FT-IR and FT-Ra ... phosphates, ASnFe(PO4)3[A | (322.5Kb) |
Abstract: | Zinc oxide (ZnO) thin films were deposited on quartz, silicon, and polymer substrates by pulsed laser deposition (PLD) technique at different oxygen partial pressures (0.007 mbar to 0.003 mbar). Polycrystalline ZnO films were obtained at room temperature when the oxygen pressure was between 0.003 mbar and .007 mbar, above and below this pressure the films were amorphous as indicated by the X-ray diffraction (XRD). ZnO films were deposited on Al2O3 (0001) at different substrate temperatures varying from 400oC to 600oC and full width half maximum (FWHM) of XRD peak is observed to decrease as substrate temperature increases. The optical band gaps of these films were nearly 3.3 eV. A cylindrical Langmuir probe is used for the investigation of plasma plume arising from the ZnO target. The spatial and temporal variations in electron density and electron temperature are studied. Optical emission spectroscopy is used to identify the different ionic species in the plume. Strong emission lines of neutral Zn, Zn+ and neutral oxygen are observed. No electronically excited O+ cations are identified, which is in agreement with previous studies of ZnO plasma plume. |
URI: | http://dyuthi.cusat.ac.in/purl/789 |
Files | Size |
---|---|
SPIE paper.pdf | (1.287Mb) |